叶片荧光渗透检测背景过度的产生原因及改进方法

详细信息

Reason and Improvement Method of Excessive Background in Fluorescent Penetrant Inspection of Vanes

摘要: 某机压气机转子叶片在荧光渗透检测时发现荧光背景过度的现象，经过第一次除氧化膜和第二次除氧化膜返修处理后，查找出背景过度的原因是叶片表面氧化膜未去除干净。因此，在压气机转子叶片的荧光渗透检测前增加了目视检查工艺，确保叶片表面氧化膜去除干净。
- 荧光渗透检测 /
- 氧化膜 /
- 预清洗 /
- 荧光背景过度
Abstract: The fluorescence background of compressor rotor blade is excessive when it is detected by fluorescence penetrant inspection. After the first and the second removing of the oxide film, the cause of excessive background is that the oxide film on the surface of the blade is removed incompletely. Therefore, a visual inspection process is added before the fluorescent penetration test of the compressor rotor blade to ensure the surface oxidation of the blade is removed completely.
- fluorescent penetrant inspection /
- oxidation film /
- prewashing /
- excessive fluorescent background

[1]	周菊元,王于梅,陈金伟. 大型铝叶片压差铸造工艺[J]. 热加工工艺,1990(3):56-58.
[2]	章海霞,李中奎,许并社,等. 氧化膜结构及内应力对新锆合金腐蚀机理的影响[J]. 金属学报,2014, 50(12):1529-1537.
[3]	黄军林,周克毅,边彩霞,等. 锅炉过热器蒸汽侧氧化膜的应力状态分析[J]. 中国电机工程学报,2012, 32(14):49-52.