Influencing Factors of the Attenuation Coefficient of the Ultrasonic Testing for Composite Porosity
-
摘要: 针对复合材料孔隙率检测需求，研究超声检测参数和被检测材料本身对超声检测衰减系数的影响，间接推断出衰减幅度的影响因素。开展了检测频率、探头类型、检测水距、材料种类对复合材料声波衰减系数的影响试验。结果表明，检测频率越高衰减系数越大，探头声束宽度越大衰减系数越大，不同材料体系的声衰减系数不同。Abstract: The influencing factors of the attenuation coefficient for porosity testing of composite are studied in this article. The experiments of changing the test frequency, probe type, water distance and the material to measure the influence to the attenuation coefficients are done. The results show that the higher the detection frequency,the bigger the attenuation coefficient, the bigger the probe beam width,the bigger the attenuation coefficient, and the acoustic attenuation coefficient of different material systems is different.
-
Keywords:
- composite /
- porosity /
- attenuation coefficient /
- influencing factor /
- ultrasonic testing
-
-
[1] ADAMS R D,CAWLEY P. Areview of defect types and nondestructive testing techniques for composites and bonded joints[J]. NDT and E International,1988,21:208-222.
[2] ACHENBACH J D. Quantitative nondestructive evaluation[J]. International Journal of Solids and Structures, 2000,37:13-27.
[3] STONE D E W, CLARKE B. Ultrasonic attenuation as a measure of void content in carbon-fibre reinforced plastics[J]. Nondestructive Testing, 1975, 8:137-145.
[4] MATIN B G.Ultrasonic wave propagation in fiber-reinforced solids containing voids[J]. Journal of Applied Physics, 1977,48:3368-3373.
[5] REYNOLDS W N, WILKINSON S J.The analysis of fibre-reinforced porous composite materials by the measurement of ultrasonic wave velocities[J].Ultrasonics, 1978,16:159-163.
[6] HALE J M, ASHTON J N. Ultrasonic attenuation in voided fibre reinforced plastics[J].NDT International, 1988,21:321-326.
[7] DANIEL I M, WOOH S C, KOMSKY I.Quantitative porosity characterization of composite materials by means of ultrasonic attenuation measurements[J]. Journal of Nondestructive Evaluation, 1992,11:1-8.
[8] JEONG H, HSU D K.Experimental analysis of porosity-induced ultrasonic attenuation and velocity change in carbon composites[J]. Ultrasonics, 1995,33:195-203.
[9] LIN L, CHEN J, ZHANG X,et al.A novel 2-D random void model and its application in ultrasonically determined void content for composite materials[J]. NDT and E International,2011,44:254-260.
[10] TITTMANN B R, AHLBERG L A, FERTIG K W.Ultrasonic microstructural noise parameters in a powder metal alloy[J]. Review of Progress in Quantitative Nondestructive Evaluation,1984, 3A:57-63.
[11] KOGAN V G, HSU D K, ROSE J H. Characterization of flaws using the zeroes of the real and imaginary parts of the ultrasonic scattering amplitude[J]. Journal of Nondestructive Evaluation,1985,5:57-68.
[12] 何方成,史亦韦.树脂基复合材料孔隙率超声表征技术研究[J].航空材料学报,2006,26(3):355-356.
计量
- 文章访问数: 8
- HTML全文浏览量: 0
- PDF下载量: 2
下载: